GARBAFLEX CrSi91

Flat and shaped wire for surface nitriding

GARBAFLEX CrSi91 is especially intended for application requiring extremely high fatigue properties and good relaxation properties at increased working temperatures.

Chemische Zusammensetzung

C (%) Si (%) Mn (%) Cr (%) V (%) Mo (%) P max. (%) S max. (%)
0,50 - 0,70 1,80 - 2,20 0,30 - 0,60 0,80 - 1,00 0,05 - 0,15 0,05 - 0,15 0,020 0,020

Mechanische Eigenschaften

Für flachgewalzten Draht

Breite (mm) Toleranz (mm)
1,00 - 5,00 ±0,050
5,01 - 8,00 ±0,070
8,01 - 10,00 ±0,100
Dicke (mm) Toleranz (mm)
0,30 - 0,80 ±0,013
0,81 - 1,00 ±0,019
1,01 - 1,60 ±0,025
1,61 - 2,30 ±0,050

Für Profildraht

Breite (mm) Toleranz (mm)
- 1,50 ±0,020
1,51 - 3,00 ±0,030
3,01 - 5,00 ±0,040
5,01 - 7,00 ±0,050
7,01 - ±0,060

Mikrostruktur

Tempered martensite with no ferrite.

Ausführung

Rolled on 2 sides (flat).
Rolled on 4 sides (shaped).
Profile drawn (shaped).

Säbelformigkeit

Max. 4 mm measured on 1 m length.

Coil set

Max. 20 mm measured on 1 m length.

Oberflächenbeschaffenheiten

Oberfläche

Bright or oxide.
Surface defects max. 1% of thickness.

Physikalische Eigenschaften

E und G Elastizitätsmodul

206 kN/mm²

E und G Schubmodul

79.5 kN/mm²

Empfehlungen

Sanftes Kugelstrahlen

Before the nitriding process a soft shot peening process shall be applied in order to remove the oxide layer on the spring wire surface.

Nitrieren

GARBAFLEX CrSi91 should be nitrided to obtain optimum fatigue and relaxation properties. Our recommendation is gas nitriding.

Zusätzlich

Zusätzliche Informationen

Decarburisation
No total decarburisation. Partial decarburisation (no continuous zones) max. 1.2% of a corresponding round wire dimension.